Release film for garment formingIt has strong toughness, wear resistance and weather resistance, excellent tensile property, anti UV polymer and anti yellowing. After installation, it can isolate the car paint from the air, prevent acid rain, oxidation and scratch, and protect the car paint for a long time. PET release film used in this field should have stable release force, high cleanliness of film surface and high Light transmittance.

Product model

Substrate thickness(μm)

Release force(gf/inch)

Haze(%)

Light transmittance(%)

F3008A

50/75

250±50

≤5

≥88

F3028Y

50/75

300±100

≤5

≥88


Car clothes maskIt is the same as the release film for garment forming, which requires stable release force, high cleanliness of film surface and high Light transmittance.

Product model

Type

Substrate thickness(μm)

Release force(gf/inch)

Haze(%)

Light transmittance(%)

C05-T10

Organosilicon

50

80-150

1.2

91

C05-T15

Organosilicon

50

100-200

1.2

91

C05-T50

Organosilicon

50

450-550

1.2

91

C42-7762X

Organosilicon

50

100-200

≤3

≥90

CPT20

Non silicon

50

400-600

≤3

≥90

CPT140A

Non silicon

50

1200-2000

≤3

≥90

F3020T

Non silicon

50

1800-2400

≤3

≥90


Car bottom filmIt is prepared with matt base film, with high scratch resistance and easy peeling; The mask has a high Light transmittance, which is close to the TPU self repairing coating without bubbles.

Product model

Substrate thickness(μm)

Normal temperature release force(gf/inch)

Haze(%)

Remnant(%)

HT4

75/85/92

45±10

80-100

≥85

HT6

75/85/92

65±15

80-100

≥85


Building window film and automobile window filmCombining building film materials with doors and windows can significantly improve the thermal insulation and energy saving characteristics of buildings, while also bringing a clear and low reflective experience. PET release membranes used in products in this field require higher Light transmittance and lower Haze.

Product model

Substrate thickness(μm)

Release force(gf/inch)

Haze(%)

Light transmittance(%)

C05-T1

23

10-20

1.2

91

C05-T3

23

25±10

≤3

≥90