Double sided tapeThis field requires PET release film to have high coating uniformity, high residual adhesion, smoothness and high cleanliness.
Product model | Substrate thickness（μm） | Release force（gf/inch） | Remnant（%） |
6612 | 25 | 6±3 | ≥88 |
C01-T1 | 25/38/50 | 13±3 | ≥88 |
CT3 | 75 | 25±10 | ≥88 |
Single-sided adhesive tapeThis field requires that the PET release membrane has stable release force, resistance to atmospheric exposure, high temperature and humidity, and non transferability.
Product model | Substrate thickness（μm） | Release force（gf/inch） | Remnant（%） |
CT1G | 36/50 | 13±3 | ≥88 |
LAT1 | 25/38 | 13±3 | ≥88 |
Foam tapePET release film used for products in this field should have stable release force and high residual rate.
Product model | Substrate thickness（μm） | Release force（gf/inch） | Remnant（%） |
CT2 | 50 | 17±6 | ≥88 |
Ultra thin tapePET release film used for products in this field should have stable release force and high residual rate.
Product model | Substrate thickness（μm） | Release force（gf/inch） | Remnant（%） |
6612 | 25 | 6±3 | ≥88 |
25XSCT1 | 25 | 13±3 | ≥88 |
Light shielding tape
PET release film used for products in this field should have stable release force and high residual rate.
Product model | Substrate thickness（μm） | Release force（gf/inch） | Remnant（%） |
CT3 | 75 | 25±10 | ≥88 |
Other special tapes
PET release film used for products in this field should have stable release force and high residual rate.
| Product model | Substrate thickness（μm） | Release force（gf/inch） | Remnant（%） |
7703 | 50 | 10±3 | ≥85 |
8323 | 50 | 10±3 | ≥88 |
Release film for FPC protective filmThe PET release film used for products in this field has high requirements for cleanliness, stable peeling force, and will not damage FPC during peeling; After stripping, the FPC surface is free of residue and pollution.
Product model | Substrate thickness（μm） | Release force（gf/inch） | Haze（%） | Light transmittance（%） |
F3008B | 50/75 | 250±50 | ≤5 | ≥88 |
PU protective film release filmThe products in this field are mainly used for the high temperature process protection of LCD panels, and the shipment protection of ITO and glass panels. The PET release film used for this product requires high Light transmittance, strong weather resistance, low adhesion, easy tear off, no silicon residue, and high temperature resistance.
Product model | Substrate thickness（μm） | Release force（gf/inch） | Haze（%） | Light transmittance（%） |
CT2F | 50/75 | 17±6 | ≤5 | ≥88 |